1008 Cold Rolled Steel Coil

1008 carbon steel coil is primarily used in extruded, cold headed, cold upset, and cold pressed parts and forms. 1008 in the cold rolled condition is used for exposed or unexposed parts where bending, moderate drawing, forming and welding may be involved.

+8619153115539

sales@chengshunmetal.com

E-mail

Submit Message

Product Details

1008 Cold Rolled Steel Coil

1008 cold rolled steel coil contains about 1.2% manganese and 0.4% silicon. There are also nickel, aluminium, chromium, copper and molybdenum present in small quantities in the carbon steels. AISI 1008 carbon steel coil has excellent weldability, which includes projection, butt, spot and fusion, and brazeability. 1008 cold rolled steel coil is mainly used in automobile, printed metal pail, building, building materials, and bicycle, etc. Besides, it is the best material to manufacture organic coated strip.

Product Parameters

Product Name	1008 Cold Rolled Steel Coil
Production Process	Hot Rolling, Cold Rolling
Material Standards	AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, etc.
Width	100mm-3000mm
Length	1m-12m, or Customized Size
Thickness	0.1mm-400mm
Delivery Conditions	Rolling, Annealing, Quenching, Tempered or Standard
Surface Process	Ordinary, Wire Drawing, Laminated Film

Chemical Composition

Element	Content (%)
Iron, Fe	99.31-99.7 %
Manganese, Mn	0.30-0.50 %
Carbon, C	0.10 %
Sulfur, S	0.050 %
Phosphorous, P	0.040 %

Mechanical Properties

Properties	Metric	Imperial
Tensile strength	340 MPa	49300 psi
Yield strength (depending on temper)	285 MPa	41300 psi
Elastic modulus	190-210 Gpa	27557-30458 ksi
Bulk modulus (typical for steel)	200 GPa	29000 ksi
Shear modulus (typical for steel)	80.0 GPa	11600 ksi
Poisson’s ratio	0.27-0.30	0.27-0.30
Elongation at break (in 50 mm)	20 %	20 %
Reduction of area	45 %	45 %
Hardness, Brinell	95	95
Hardness, Knoop (converted from Brinell hardness)	113	113
Hardness, Rockwell B (converted from Brinell hardness)	55	55
Hardness, Vickers (converted from Brinell hardness)	98	98
Machinability (based on AISI 1212 steel as 100 machinability) The machinability of group I bar, rod, and wire products can be improved by cold drawing)	55	55

Scope of Application

AISI 1008 carbon steel is primarily used in extruded, cold headed, cold upset, and cold pressed parts and forms.

Product Picture

Packaging and transportation&Customer feedback

Product Certificate

Shandong Chengshun Metal Materials Co., Ltd.is a comprehensive company dealing in high-quality steel products, with a superior geographical location and very convenient transportation. The company has a complete and scientific quality system, and has been recognized by the industry for its integrity, strength and product quality. Always adhere to the tenet of high quality, low cost, fast pace and excellent service. Our products have passed the "IS09001" qualtly system cerification, own CE cerificate and SGS test report.

APPLICATION FIELD

Our main manufactures are stainless steel, galvanized steel, carbon steel and etc. That apply to engineering, coal mine, textile, electric power, boiler, machinery, We stick to the principle of "quality first, service first, continuous improvement and innovation to meet the customers" for the management and "zero defect, zero complaints" as the quality objective. We′re pleased to get your Inquiry and we will come back to as soon as possible.

mechanical

power plant

chemical plant

Oil Pipelines

Natural Gas Pipeline

refrigeration equipment

boiler plant

Chemical plant

Water pipes

Bearing